LA133 veziva na bazi vode za litij-jonske baterijske sirovine

Stacking Machine For Battery.jpg产品信息.jpg

Tob-LA132 / LA133 na bazi vode na bazi vode je vrsta vodene otopine akrilonitrilnog kopolimera koja ima dobru toplotnu i elektrohemijsku stabilnost. Prikladni su za katodne i anodermalne materijale raznih litijum-jonskih baterija.

Specifikacije

Predmet

Model


LA132

LA133


Viskoznost (mPa · S , 40 ℃)

≥4800

7300~9300

D50(μm)

≤1.2

≤1.0

Čvrsti sadržaj (%)

15±0.2

15±0.2

pH

7~9

7~9

Izgled

Mlečno bela ili žućkasta vodena emulzija


Bilješka:

● Viskoznost LA132 / LA133 veziva je velika. Dodajte deioniziranu vodu ili destilovanu vodu kako biste je razrijedili polako prije upotrebe, ona će biti korisna za disperziju.

● Dodavanje PC ili EC suspenziji anode pripremljenoj u vezivu LA132 / LA133 može povećati mekoću elektrode i izbeći namotavanje i pucanje ivica. Količina je oko 5% ukupne količine otapala.

● Preporučuje se da se maksimalna temperatura jednog bočnog premaza LA132 i LA133 suspenzije kontroliše ispod 80 ℃. Ako je temperatura u pećnici previsoka, to može prouzročiti pucanje ivica i pucanje premaza.

● Tokom trajanja, viskozitet La vezivnog proizvoda raste sa vremenom skladištenja, to je normalno.


Primjena:Koristite za vezivo za litijum-jonske baterije, također možete razmotritiPTFE, SBR,PVDF.



Battery Winding Machine

Water Based LA133 Binder For Lithium ion Battery Raw Material Stacking Machine For Battery.jpg产品信息.jpg  Tob-LA132 / LA133 water-based binder is a kind of water solution of acrylonitrile copolymer, which has good thermal stability and electrochemical stability. It’s suitable for cathode and anode materials of various lithium-ion batteries.  MOQ: 500g/bottle, 30usd/bottle.  Specifications  Item  Model  LA132  LA133  Viscosity (mPa·S,40℃)  ≥4800  7300~9300  D50(μm)  ≤1.2  ≤1.0  Solid Content (%)  15±0.2  15±0.2  pH  7~9  7~9  Appearance  Milk white or yellowish water emulsion     Note:  ● The viscosity of LA132 / LA133 binder is large. Add deionized water or distilled water to dilute slowly before use, it will be beneficial to dispersion.  ● Adding PC or EC to the anode slurry prepared by LA132 / LA133 binder can increase the softness of the electrode and avoid the edge winding and cracking. The amount is about 5% of the total solvent amount.  ● The maximum single side coating temperature of LA132 and LA133 slurry is suggested to be controlled below 80 ℃. If the oven temperature is too high, maybe cause edge curling and coating cracking.  ● During the shelf life, the viscosity of La binder product increases with storage time, it is normal.    Battery Winding Machine  T-SBR-50 (2)    6.jpg    证书.jpg

6.jpg


证书.jpg



Hot Tags: vodeno vezivo na bazi la133, dobavljači, proizvođači, tvornica, cijena

Upit

You Might Also Like